Here’s what the shattered panel I posted about that had damage in the kiln looks like, there’s so many tiny fragments that I determined in about 10 minutes of trying to see if it can be repaired to some extent that it’s beyond that LOL. If it was just a few large fragments it wouldn’t be hard to piece back together, but there’s a gallon pail full of dime sized chips and fragments too that are not shown.
That’s ok though since I have a mold of it, still, it would have been nice to put back together, but with the amount of fragmentation, and then that wide crack- the fragments would never seat and lock back in the way they were- the “background” for them has obviously expanded and changed, which is what opened that crack.